Titanium Socket Head Cap Screws – Complete Product Range

Critical Applications of Titanium Socket Head Cap Screws

International Standards & Global Designations – Titanium Socket Screw Materials

RAYCHIN LIMITED manufactures Titanium socket head cap screws from material conforming to the most widely used national and international specifications. All material is traceable to the mill.

Chemical Composition (Weight %) – Titanium Alloys for Socket Head Cap Screws

Our Titanium socket head cap screws are produced from material conforming to the limits of applicable ASTM, AMS, and ISO standards. High‑purity grades available for medical and semiconductor applications.

Commercially Pure Titanium (Grades 1-4) – ASTM B348 / F67

Titanium Alloys – ASTM B348 / F136

Metallurgical note: Titanium is an allotropic element with a hexagonal close-packed (α) structure at room temperature, transforming to body-centered cubic (β) at 882°C. CP grades are α-phase, while alloying with aluminum stabilizes α-phase, and vanadium/molybdenum stabilize β-phase. Ti-6Al-4V is an α+β alloy combining high strength with good ductility. The natural oxide layer (TiO₂) is 2-5 nm thick, self‑healing, and responsible for titanium's exceptional corrosion resistance. Titanium is non‑magnetic with magnetic permeability <1.00005, essential for medical and aerospace applications.

Complete Mechanical & Physical Properties – Titanium Alloys for Socket Head Cap Screws (MPa / ksi)

Titanium socket head cap screws are supplied in appropriate conditions (annealed for CP grades, solution treated and aged for Grade 5) per ASTM B348, ASTM F136, and customer specifications. Data represent typical values based on industry standards.

Commercially Pure Titanium – Mechanical Properties (minimum values)

Titanium Alloys – Mechanical Properties (minimum values)

High‑Temperature Mechanical Properties – Ti-6Al-4V (typical values)

Note: Prolonged exposure above 300°C may cause oxidation; protective coatings recommended above 500°C.

Physical Properties – Titanium

High‑Temperature Performance of Titanium Socket Head Cap Screws

Titanium alloys retain significant strength at elevated temperatures up to 500°C, making them suitable for aerospace and industrial applications. Ti-6Al-4V maintains useful mechanical properties up to 315°C (600°F) for extended service, and up to 500°C (932°F) for short-term exposure. The alloy exhibits excellent creep resistance at moderate temperatures. However, titanium becomes increasingly reactive with oxygen above 500°C, forming an oxygen-enriched brittle α-case layer that degrades fatigue life. For applications above 500°C, protective coatings (such as TiAlN) or high-temperature alloys (Ti-6242, Ti-1100) are recommended. Titanium's melting point (1660°C) is higher than steel, but oxidation limits practical use in air. The socket head design maintains drive integrity at elevated temperatures.

Elevated Temperature Capabilities

Note: Titanium alloys are susceptible to "alpha case" formation above 500°C in air, which embrittles the surface.

Exceptional Corrosion Resistance of Titanium Socket Head Cap Screws

Titanium is renowned for its outstanding corrosion resistance in a wide range of environments, often exceeding that of stainless steels and nickel alloys. The protective TiO₂ oxide film (2-5 nm thick) is stable in oxidizing media and rapidly self‑heals if damaged. Titanium is virtually immune to pitting, crevice corrosion, and stress corrosion cracking in chloride environments up to 200°C.

• Seawater / Marine: Titanium is completely resistant to seawater up to 120°C. Corrosion rate <0.01 mm/year in flowing seawater, with no measurable attack after decades of immersion. Immune to crevice corrosion in ambient seawater.
• Chlorides: Excellent resistance to chlorides, hypochlorites, and chlorine dioxide. Used in chlorine bleach plants and seawater desalination.
• Nitric Acid: Outstanding resistance up to boiling temperatures at all concentrations. Corrosion rate <0.1 mm/year.
• Acetic Acid: Excellent resistance at all concentrations and temperatures up to boiling.
• Sulfuric Acid: CP titanium resistant up to 5% at boiling, 10% at ambient. Grade 7 (Pd) extends resistance to 40% at boiling.
• Hydrochloric Acid: CP titanium resistant up to 3% at boiling, 8% at ambient. Grade 7 extends to 20% at ambient, 7% at boiling.
• Phosphoric Acid: CP titanium resistant up to 20% at ambient. Grade 7 extends to 40% at ambient, 10% at boiling.
• Organic Acids: Completely resistant to all organic acids, including formic, citric, and tartaric acids.
• Alkalis: Resistant to dilute alkalis at ambient. Attacked by concentrated hot alkalis.
• Halogens: Resistant to wet chlorine gas and chlorine solutions. Not recommended for dry chlorine above 200°C.
• Hydrofluoric Acid: Rapidly attacked by HF and fluoride-containing media – not recommended.
• Galvanic Corrosion: Titanium is cathodic to most metals; can accelerate corrosion of active metals (steel, aluminum) in contact. Isolation or coating recommended.
• Hydrogen Embrittlement: Titanium can absorb hydrogen in certain conditions (cathodic charging, acid pickling). Grades with Pd or Ru reduce hydrogen pickup.

Manufacturing Standards – Titanium Socket Head Cap Screws

All Titanium socket head cap screws are manufactured and tested to meet the following standards:

We offer surface finishes: plain (as‑machined), passivated, anodized, and silver plating per AMS 2410 for anti‑seize and galvanic corrosion prevention. Titanium socket head cap screws can be supplied with certified material traceability, dimensional inspection reports, and mechanical test certificates. Our manufacturing processes include CNC heading, thread rolling, and heat treatment (solution treat and age for Grade 5). We specialize in custom configurations including non‑standard lengths, special head markings, and proprietary thread forms. Cleanroom packaging available for medical and semiconductor applications. All screws supplied with EN 10204 Type 3.1 or 3.2 certification. ISO 9001:2015 and AS9100D certified quality management system.